29 May 2022>: Database Analysis
Effect of Thermocycling on Color, Surface Characteristics, Compressive Fracture, and Fracture Modes of Prosthetic CAD/CAM Ceramics After Smokeless Tobacco Immersion
Saeed M. Alqahtani ABCDEFG*DOI: 10.12659/MSM.936885
Med Sci Monit 2022; 28:e936885
Table 2 ANOVA test values for Ra and Rz of the used prosthetic materials.
Parameter | Sum of squares | df | Mean square | F | p-value | |
---|---|---|---|---|---|---|
Ra before immersion & TC | Between groups | 0.208 | 2 | 0.104 | 112.321 | |
Within groups | 0.042 | 45 | 0.001 | |||
0.250 | 47 | |||||
Ra after immersion without TC | Between groups | 0.55 | 2 | |||
Within groups | ||||||
Ra after immersion & with TC | Between groups | |||||
Within groups | ||||||
Rz before immersion & TC | Between groups | |||||
Within groups | ||||||
Rz after immersion without TC | Between groups | |||||
Within groups | ||||||
Rz after immersion & with TC | Between groups | |||||
Within groups | ||||||